CN103804951A - Wisteria-colored wheat straw dye and production method thereof - Google Patents
Wisteria-colored wheat straw dye and production method thereof Download PDFInfo
- Publication number
- CN103804951A CN103804951A CN201410077126.9A CN201410077126A CN103804951A CN 103804951 A CN103804951 A CN 103804951A CN 201410077126 A CN201410077126 A CN 201410077126A CN 103804951 A CN103804951 A CN 103804951A
- Authority
- CN
- China
- Prior art keywords
- wheat straw
- wisteria
- raw material
- iron ion
- ion compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a wisteria-colored wheat straw dye and a production method thereof. According to the wisteria-colored wheat straw dye, blackberries, cornflower petals, salix pseudotangii, white alum, an iron ion compound solution and mineral water are taken as main raw materials. The production method of the wisteria-colored wheat straw dye comprises the main process flows of selecting the materials, cutting the materials, drying, soaking, cooking, mixing, precipitating, dyeing and finishing a product. The wisteria-colored wheat straw dye is purely natural, pollution-free and environmentally friendly, is free from toxic and side effects on human bodies and is prepared from purely-natural plants.
Description
technical field:
the present invention relates to a kind of vegetable dye, particularly relates to one and prepares wisteria Wheat Straw dye well production method.
background technology:
in prior art, the method of the main raw material Wheat Straw of making straw patchwork being dyed to wisteria has a variety of, but most dyestuffs are chemical dye, the wisteria dyeing is impure, easily fade, not only not environmental protection, part dyestuff even can produce toxic gas in the process of the system of dying, and threatens the health of human body.
thereby, lack a kind of vegetable dye of Wheat Straw being dyed to different colours in straw patchwork making field, particularly Wheat Straw is dyed to the natural plant dyestuff of wisteria, not only color is pure for the wisteria Wheat Straw that it dyes, and the straw patchwork made from its material is bright and new beautiful, is difficult for fading, and environmental protection, works give out plant delicate fragrance for a long time, have easy people's physical and mental health, the solution that degree is different other poisonous and harmful chemical dye dying the harm in process processed, people's health being caused.
summary of the invention:
the one being mixed with natural plant that the object of the present invention is to provide a kind of pure natural, pollution-free, environmental protection, the person is had no side effect is prepared wisteria Wheat Straw dye well production method.
the object of the present invention is achieved like this.It is that the raw material of being joined by following weight is made, blackberry, blueberry 25-40 part, Minor centaury petal 10-30 part, Black Hills willow 5-15 part, alum 5-15 part, iron ion compound solution 5-15 part, mineral water 30-80 part.
preparing wisteria Wheat Straw dyestuff preferred weight ratio range of the present invention is, wherein the weight proportion of various raw materials is, blackberry, blueberry 25-35 part, Minor centaury petal 10-25 part, Black Hills willow 5-10 part, alum 5-10 part, iron ion compound solution 5-10 part, mineral water 30-70 part.
the optimum weight ratio range of preparing wisteria Wheat Straw dyestuff of the present invention is that wherein the weight proportion of various raw materials is: 30 parts of blackberry, blueberry, 15 parts, Minor centaury petal, 7 parts, Black Hills willow, 8 parts of alums, 7 parts of iron ion compound solutions, 60 parts of mineral waters.
above-mentioned each component is made to the production method of wisteria Wheat Straw dyestuff of the present invention, technical process is: select materials, blank, oven dry, immersion, heat boil, mix, precipitation, dyeing, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select that to meet blackberry, blueberry, Minor centaury petal, Black Hills willow, alum, iron ion compound solution, the mineral water of national health and quality standard for subsequent use; B, blank, the raw material of selecting is cut into respectively to bulk except alum, iron ion compound solution, mineral water; C, oven dry, will be cut into block raw material and be placed in respectively stoving oven mummification, temperature is controlled at 100-120 ℃, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in to the storage tank that mineral water is housed soaks, temperature is 20 ℃ of chambers, time 2-4 hour; E, heat are boiled, the raw material steeping are pulled out from water, are put into pottery interior heat and boil, and 6 hours time, cook pigment solution; F, mixing, pigment solution is invaded in 20% iron ion compound solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool mixing solutions to 20 ℃, be settled out pure wisteria cellulose solution; H, dyeing, the temperature of 100 liters of pure wisteria cellulose solutions is raised to more than 80 ℃ gradually, to soak wherein through sterilization, desulfurization, boiling Wheat Straw after treatment, constant temperature leaves standstill 12-14 hour, during this time Wheat Straw is stirred up and down, make Wheat Straw fully absorb wisteria cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution that adds alum powder, soak 3-6 hour, make to pull out after the abundant fixation of Wheat Straw, drench dryly, be slowly dried at room temperature wisteria Wheat Straw finished product.
the invention has the advantages that: 1, select raw material, scientific formulation, color is pure; 2, in product, do not add sanitas, industrial chemicals, pure natural, to human body, without any injury, the straw patchwork works made from its raw material not only distribute Scent, and anticorrosive; 3 raw material sources are extensive, add technique circuit short, the easy processing and manufacturing of product.
Embodiment
below in conjunction with specific embodiment, the present invention is further illustrated:
embodiment 1:
preparing wisteria Wheat Straw dyestuff weight proportion scope of the present invention is: blackberry, blueberry 25-40 part, Minor centaury petal 10-30 part, Black Hills willow 5-15 part, alum 5-15 part, iron ion compound solution 5-15 part, mineral water 30-80 part.
embodiment 2:
preparing wisteria Wheat Straw dyestuff preferred weight ratio range of the present invention is: blackberry, blueberry 25-35 part, Minor centaury petal 10-25 part, Black Hills willow 5-10 part, alum 5-10 part, iron ion compound solution 5-10 part, mineral water 30-70 part.
embodiment 3:
preparing wisteria Wheat Straw dyestuff optimum weight ratio range of the present invention is: 30 parts of blackberry, blueberry, 15 parts, Minor centaury petal, 7 parts, Black Hills willow, 8 parts of alums, 7 parts of iron ion compound solutions, 60 parts of mineral waters.
above-mentioned each component is made to the production method of wisteria Wheat Straw dyestuff of the present invention, technical process is: select materials, blank, oven dry, immersion, heat boil, mix, precipitation, dyeing, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select that to meet blackberry, blueberry, Minor centaury petal, Black Hills willow, alum, iron ion compound solution, the mineral water of national health and quality standard for subsequent use; B, blank, the raw material of selecting is cut into respectively to bulk except alum, iron ion compound solution, mineral water; C, oven dry, will be cut into block raw material and be placed in respectively stoving oven mummification, temperature is controlled at 100-120 ℃, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in to the storage tank that mineral water is housed soaks, temperature is 20 ℃ of chambers, time 2-4 hour; E, heat are boiled, the raw material steeping are pulled out from water, are put into pottery interior heat and boil, and 6 hours time, cook pigment solution; F, mixing, pigment solution is invaded in 20% iron ion compound solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool mixing solutions to 20 ℃, be settled out pure wisteria cellulose solution; H, dyeing, the temperature of 100 liters of pure wisteria cellulose solutions is raised to more than 80 ℃ gradually, to soak wherein through sterilization, desulfurization, boiling Wheat Straw after treatment, constant temperature leaves standstill 12-14 hour, during this time Wheat Straw is stirred up and down, make Wheat Straw fully absorb wisteria cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution that adds alum powder, soak 3-6 hour, make to pull out after the abundant fixation of Wheat Straw, drench dryly, be slowly dried at room temperature wisteria Wheat Straw finished product.
Claims (4)
1. prepare wisteria Wheat Straw dyestuff for one kind, it is characterized in that: it is to be made up of the raw material of following weight proportioning blackberry, blueberry 25-40 part, Minor centaury petal 10-30 part, Black Hills willow 5-15 part, alum 5-15 part, iron ion compound solution 5-15 part, mineral water 30-80 part.
2. prepare wisteria Wheat Straw dyestuff for one kind, it is characterized in that: wherein the weight proportion of various raw materials is blackberry, blueberry 25-35 part, Minor centaury petal 10-25 part, Black Hills willow 5-10 part, alum 5-10 part, iron ion compound solution 5-10 part, mineral water 30-70 part.
3. prepare a wisteria Wheat Straw dyestuff, it is characterized in that: wherein the weight proportion of various raw materials is, 30 parts of blackberry, blueberry, 15 parts, Minor centaury petal, 7 parts, Black Hills willow, 8 parts of alums, 7 parts of iron ion compound solutions, 60 parts of mineral waters.
4. according to a kind of production method of preparing wisteria Wheat Straw dyestuff described in claim 1-3, it is characterized in that: technical process is: select materials, blank, oven dry, immersion, heat boil, mix, precipitation, dyeing, finished product, concrete operation method follows these steps to successively: A, select materials, by raw material weight proportioning, select that to meet blackberry, blueberry, Minor centaury petal, Black Hills willow, alum, iron ion compound solution, the mineral water of national health and quality standard for subsequent use; B, blank, the raw material of selecting is cut into respectively to bulk except alum, iron ion compound solution, mineral water; C, oven dry, will be cut into block raw material and be placed in respectively stoving oven mummification, temperature is controlled at 100-120 ℃, 30 minutes time, evaporation raw material moisture content, sterilizing; D, immersion, the raw material after drying is placed in to the storage tank that mineral water is housed soaks, temperature is 20 ℃ of chambers, time 2-4 hour; E, heat are boiled, the raw material steeping are pulled out from water, are put into pottery interior heat and boil, and 6 hours time, cook pigment solution; F, mixing, pigment solution is invaded in 20% iron ion compound solution, time 4-8 hour, makes mixing solutions; G, precipitation, by cool mixing solutions to 20 ℃, be settled out pure wisteria cellulose solution; H, dyeing, the temperature of 100 liters of pure wisteria cellulose solutions is raised to more than 80 ℃ gradually, to soak wherein through sterilization, desulfurization, boiling Wheat Straw after treatment, constant temperature leaves standstill 12-14 hour, during this time Wheat Straw is stirred up and down, make Wheat Straw fully absorb wisteria cellulose solution, level dyeing; I, fixation, the Wheat Straw after dyeing is put into the solution that adds alum powder, soak 3-6 hour, make to pull out after the abundant fixation of Wheat Straw, drench dryly, be slowly dried at room temperature wisteria Wheat Straw finished product.